Peroxide crosslinkable strippable Semi-conductive shielding material for insulation layer of 35kV and below XLPE cables
Peroxide crosslinkable strippable Semi-conductive shielding material for insulation layer of 35kV and below XLPE cables
Unleash Efficiency and Performance with our Strippable Semi-Conductive Shielding Material! Tailored for XLPE Cables up to 35kV, Experience the Future of Insulation Innovation. Free Samples Are Available.
PAYMENT TERMS T/T, L/C, D/P, etc.
DELIVERY TIME 10 days
SHIPPING By sea
PORT OF LOADING Shanghai, China
HS CODE 3901909000
STORAGE 12 months
Product Introduction
This product is applicable for strippable insulation shielding of 35kV and below XLPE insulated cables. It is manufactured with importing raw materials by Swiss BUSS extrusion equipment through compounding process.
The surface of the cables is smooth.
Processing Indicator
Recommend to process with the PE extruder
| Model | Machine Barrel Temperature | Molding Temperature |
|---|---|---|
| OW-YP(W)-35 | 70-115℃ | 110-117℃ |
| No | Item | Unit | Technical Requirements |
| 1 | Relative Density | g/cm³ | ≤1.20 |
| 2 | Tensile Strength | MPa | ≥12 |
| 3 | Elongation at Break | % | ≥250 |
| 4 | 20℃ Volume Resistivity | Ω·cm | ≤100 |
| 5 | 90℃ Volume Resistivity | Ω·cm | ≤1000 |
| 6 | 90℃ Volume Resistivity after air aging(100℃×168h) | Ω·cm | ≤1000 |
| 7 | Air Aging Test | / | (135±2℃)×168h |
| 8 | Tensile Strength Variation After Aging | % | ±25 |
| 9 | Elongation Variation After Aging | % | ±25 |
| 10 | Hot Set Test | / | 200℃×0.2MPa×15min |
| 11 | Hot Elongation (Hot) | % | ≤100 |
| 12 | Permanent Deformation after Cooling (Set) | % | ≤15 |
| 13 | Peel Strength 20℃ | N/cm | 10-30 |
| Note: More specifications, please contact our sales staff. | |||
| No | Item | Unit | Technical Requirements |
| 1 | Relative Density | g/cm³ | ≤1.20 |
| 2 | Tensile Strength | MPa | ≥12 |
| 3 | Elongation at Break | % | ≥250 |
| 4 | 20℃ Volume Resistivity | Ω·cm | ≤100 |
| 5 | 90℃ Volume Resistivity | Ω·cm | ≤1000 |
| 6 | 90℃ Volume Resistivity after air aging(100℃×168h) | Ω·cm | ≤1000 |
| 7 | Air Aging Test | / | (135±2℃)×168h |
| 8 | Tensile Strength Variation After Aging | % | ±25 |
| 9 | Elongation Variation After Aging | % | ±25 |
| 10 | Hot Set Test | / | 200℃×0.2MPa×15min |
| 11 | Hot Elongation (Hot) | % | ≤100 |
| 12 | Permanent Deformation after Cooling (Set) | % | ≤15 |
| 13 | Peel Strength 20℃ | N/cm | 10-30 |
| Note: More specifications, please contact our sales staff. | |||