Peroxide crosslinkable Semi-conductive shielding material for 35kV and below XLPE cables
Peroxide crosslinkable Semi-conductive shielding material for 35kV and below XLPE cables
Superior Peroxide Crosslinkable Semi-conductive Shielding Material Ensuring Top-tier Performance and Reliability.
PAYMENT TERMS T/T, L/C, D/P, etc.
DELIVERY TIME 10 days
SHIPPING By sea
PORT OF LOADING Shanghai, China
HS CODE 3901909000
STORAGE 12 months
Product Introduction
Technical Parameters
Packing Storage
Product Introduction
Product Introduction
This product is applicable for conductor shielding and non-strippable insulation shielding of 35kV and below XLPE insulated cables. It is manufactured with importing raw materials by Swiss BUSS extrusion equipment through compounding process. The surface of the cables is smooth.
Processing Indicator
Recommend to process with the PE extruder
| Model | Machine Barrel Temperature | Molding Temperature |
|---|---|---|
| OW-YP-35 | 70-115℃ | 110-117℃ |
Technical Parameters
| No | Item | Unit | Technical Requirements |
| 1 | Relative Density | g/cm³ | ≤1.20 |
| 2 | Tensile Strength | MPa | ≥12 |
| 3 | Elongation at Break | % | ≥240 |
| 4 | 20℃ Volume Resistivity | Ω·cm | ≤100 |
| 5 | 90℃ Volume Resistivity | Ω·cm | ≤1000 |
| 6 | 90℃ Volume Resistivity after air aging(100℃×168h) | Ω·cm | ≤1000 |
| 7 | Air Aging Test | / | (135±2℃)×168h |
| 8 | Tensile Strength Variation After Aging | % | ±25 |
| 9 | Elongation Variation After Aging | % | ±25 |
| 10 | Hot Set Test | / | 200℃×0.2MPa×15min |
| 11 | Hot Elongation | % | ≤100 |
| 12 | Permanent Deformation after Cooling (Set) | % | ≤15 |
| 13 | Peel Strength 20℃ | N/cm | – |
| Note: More specifications, please contact our sales staff. | |||
Packing Storage
| No | Item | Unit | Technical Requirements |
| 1 | Relative Density | g/cm³ | ≤1.20 |
| 2 | Tensile Strength | MPa | ≥12 |
| 3 | Elongation at Break | % | ≥240 |
| 4 | 20℃ Volume Resistivity | Ω·cm | ≤100 |
| 5 | 90℃ Volume Resistivity | Ω·cm | ≤1000 |
| 6 | 90℃ Volume Resistivity after air aging(100℃×168h) | Ω·cm | ≤1000 |
| 7 | Air Aging Test | / | (135±2℃)×168h |
| 8 | Tensile Strength Variation After Aging | % | ±25 |
| 9 | Elongation Variation After Aging | % | ±25 |
| 10 | Hot Set Test | / | 200℃×0.2MPa×15min |
| 11 | Hot Elongation | % | ≤100 |
| 12 | Permanent Deformation after Cooling (Set) | % | ≤15 |
| 13 | Peel Strength 20℃ | N/cm | – |
| Note: More specifications, please contact our sales staff. | |||