Insulation Material for 3kV and below Silane XLPE Cables
Insulation Material for 3kV and below Silane XLPE Cables
Experience Unmatched Excellence in Insulation: Elevate Your Cables with 3kV and Below Silane XLPE Material. Achieve Exceptional Performance and Reliability in Every Connection.
PAYMENT TERMS T/T, L/C, D/P, etc.
DELIVERY TIME 10 days
SHIPPING By sea
PORT OF LOADING Shanghai, China
HS CODE 3901909000
STORAGE 12 months
Product Introduction
Insulation Material for 3kV and below Silane XLPE Cables is two-step silane cross-linkable insulation compounds. It is mainly used for the insulation of low-voltage cables and control cables with working voltage for 3KV and below. The highest working temperature is 90℃.
It is suitable for squeeze tube mold production process.
Processing Indicator
Recommend to process with the PE extruder
| Model | Machine Barrel Temperature | Molding Temperature |
|---|---|---|
| OW-YJG(2)-3 | 155-175℃ | 180-190℃ |
| No. | Item | Unit | Technical Requirements | ||
| 1 | Density | g/cm³ | 0.922±0.005 | ||
| 2 | Tensile Strength | MPa | ≥13.5 | ||
| 3 | Elongation at Break | % | ≥350 | ||
| 4 | Brittle Temperature with Low Temperature | ℃ Failure Rate |
-76 ≤15/30 |
||
| 5 | 20℃ Volume Resistivity | Ω·m | ≥1.0×10¹⁴ | ||
| 6 | 20C Dielectric Strength,50Hz | MV/m | ≥25.0 | ||
| 7 | 20℃ Dielectric Constant,50Hz | – | ≤2.35 | ||
| 8 | Air Aging Condition 135±2℃×168h |
Tensile Strength Variation After Aging |
% | ±20 | |
| Elongation Variation After Aging |
% | ±20 | |||
| 9 | Hot Set Test Condition 200℃×0.2MPa×15min |
1mm thick 95 ℃ boiled 2 hours test |
Hot Elongation | % | ≤100 |
| Permanent Deformation after Cooling | % | ≤5 | |||
| Note: More speclfications, please contact our sales staff. | |||||
| No. | Item | Unit | Technical Requirements | ||
| 1 | Density | g/cm³ | 0.922±0.005 | ||
| 2 | Tensile Strength | MPa | ≥13.5 | ||
| 3 | Elongation at Break | % | ≥350 | ||
| 4 | Brittle Temperature with Low Temperature | ℃ Failure Rate |
-76 ≤15/30 |
||
| 5 | 20℃ Volume Resistivity | Ω·m | ≥1.0×10¹⁴ | ||
| 6 | 20C Dielectric Strength,50Hz | MV/m | ≥25.0 | ||
| 7 | 20℃ Dielectric Constant,50Hz | – | ≤2.35 | ||
| 8 | Air Aging Condition 135±2℃×168h |
Tensile Strength Variation After Aging |
% | ±20 | |
| Elongation Variation After Aging |
% | ±20 | |||
| 9 | Hot Set Test Condition 200℃×0.2MPa×15min |
1mm thick 95 ℃ boiled 2 hours test |
Hot Elongation | % | ≤100 |
| Permanent Deformation after Cooling | % | ≤5 | |||
| Note: More speclfications, please contact our sales staff. | |||||