90℃ Type I Lead-free Sheath Compound
90℃ Type I Lead-free Sheath Compound
90℃ Type I Lead-free Sheath Compound – Engineered with Advanced PVC Resin, Delivering Exceptional Mechanical, Electrical, and Processing Properties for Power Cables up to 35kV. Compliant with RoHS Standard.
PAYMENT TERMS T/T, L/C, D/P, etc.
DELIVERY TIME 10 days
SHIPPING By sea
PORT OF LOADING Shanghai, China
HS CODE 3901909000
STORAGE 12 months
Product Introduction
OW-(W)H-90 is granular compounds which is manufactured through mixing, plasticizing and pelletizing processes. It regards advanced PVC resin as the basic raw materials, and add plasticizer, stabilizer and other accessory ingredients. It has good mechanical and physical property, electrical property and excellent processing performance. It meets RoHS Standard.
It is usually used for the sheath of 26/35kV and below power cables.
Processing Indicator
Recommend to use single-screw extruders with L/D=20-25.
| Model | Machine Barrel Temperature | Molding Temperature |
|---|---|---|
| OW-(W)H-90 | 150-170℃ | 170-180℃ |
| No. | Item | Unit | Technical Requirements |
| 1 | Tensile Strength | MPa | ≥16.0 |
| 2 | Elongation at Break | % | ≥180 |
| 3 | Thermal Deformation | % | ≤40 |
| 4 | Brittle Temperature With Low Temperature Impact | ℃ | -20 |
| 5 | 200℃ Thermal Stability | min | ≥80 |
| 6 | 20℃ Volume Resistivity | Ω·m | ≥1.0×10⁹ |
| 7 | Dielectric Strength | MV/m | ≥18 |
| 8 | Thermal Aging | \ | 100±2℃×240h |
| 9 | Dielectric Tensile Strength After Aging | MPa | ≥16.0 |
| 10 | Tensile Strength Variation | % | ±20 |
| 11 | Elongation After Aging | % | ≥180 |
| 12 | Elongation Variation | % | ±20 |
| 13 | Mass Losses(100℃×240h) | g/m² | ≤15 |
| Note: More specifications, please contact our sales staff. | |||
| No. | Item | Unit | Technical Requirements |
| 1 | Tensile Strength | MPa | ≥16.0 |
| 2 | Elongation at Break | % | ≥180 |
| 3 | Thermal Deformation | % | ≤40 |
| 4 | Brittle Temperature With Low Temperature Impact | ℃ | -20 |
| 5 | 200℃ Thermal Stability | min | ≥80 |
| 6 | 20℃ Volume Resistivity | Ω·m | ≥1.0×10⁹ |
| 7 | Dielectric Strength | MV/m | ≥18 |
| 8 | Thermal Aging | \ | 100±2℃×240h |
| 9 | Dielectric Tensile Strength After Aging | MPa | ≥16.0 |
| 10 | Tensile Strength Variation | % | ±20 |
| 11 | Elongation After Aging | % | ≥180 |
| 12 | Elongation Variation | % | ±20 |
| 13 | Mass Losses(100℃×240h) | g/m² | ≤15 |
| Note: More specifications, please contact our sales staff. | |||