Deliver the Silane-XLPE Compound of Two-Step (Sioplas) Method to Thailand

Deliver the Silane-XLPE Compound of Two-Step (Sioplas) Method to Thailand

Deliver the Silane-XLPE Compound of Two-Step (Sioplas) Method to Thailand

Post time: 03-12-2021


The black Silane-XLPE compound of Sioplas method materials and thermoplastic semi-conductive shielding materials that we provided has been delivered to Thailand successfully in February of 2021. Our Thailand customer are going to test these samples’ properties. ONE WORLD has confidence in our cable materials.

In fact, our customer told us the inquiry that they are looking for the black silane-xlpe for 5kv medium voltage cables in the beginning of the communication through our official website: www.owcable.com. ONE WORLD has two color options: natural color and black (Like the below picture). After several rounds of discussion, we offered the quotation and technical data sheet to the customer with good price. In the meanwhile, we suggested that customer can try our thermoplastic semi-conductive shielding materials together with silane-xlpe materials together. Now these two materials are going to be tested together.

(10 kV Silane-XLPE Compound of Sioplas Method)

(10 kV Silane-XLPE Compound of Sioplas Method)

The silane-xlpe compound of sioplas method we provided has the characteristics of excellent electrical insulation properties, anti-aging ability and tensile strength, excellent low-temperature brittleness properties.

The highest continuous working temperature is 90 ℃.

(Package pictures before delivery)

(Package pictures before delivery)

Here is the specific technical parameters for your reference:

 

Item

Testing method

Standard value

Typical value

National

International

Appearance

Black Color

Pass

Density (g/cm3)

GB/T 1033.1-2008

ISO

1183-1:2004,IDT

0.925

Tensile strength (MPa)

GB/T 1040-2006

ISO 527:1995,IDT

≥13

23.0

Breaking elongation (%)

≥300

530

Brittleness temperature

(-76℃, 30pieces) (Piece)

GB/T 5470-2008

ISO 974:2000,MOD

≤15

0

 

Hot set

elongation

(200℃, 0.2Mpa,

15min)

Elongation

under load (%)

GB/T 2951.21-2008

IEC

60811-2-1:2001,IDT

≤175

50

Permanent deformation

after cooling (%)

≤15

0

 

Ageing (135℃, 168h)

Change of tensile strength(%)

GB/T 2951.12-1997

IEC

60811-1-2:2001,IDT

±20

-9.6

Change

of elongation (%)

±20

-8.3

DC volume resistivity (20℃) (Ω·m)

GB/T 1410-2006

IEC 60093:1980,IDT

≥5.0x1013

8.0x1013

Dielectric strength (20℃) (MV/m)

GB/T 1408.1-1999

IEC 602431:1998,IDT

≥25

34