WMA101 is a type of sioplas method moisture cured insulation material which is applied for electric wires and cables. It has advantages of excellent electrical insulation properties, anti-ageing ability and tensile strength, the highest continuous working temperature is 90℃ and excellent low-temperature brittleness property.
WMA101 must be mixed with the catalyst B material (WMA101: B=95:5).
|
Item |
Testing method |
Natural color |
Black |
||||
|
National |
International |
Standard value |
Typical value |
Standard value |
Typical value |
||
|
Density (g/cm3) |
GB/T 1033 |
ISO 1183 |
- |
0.92 |
- |
0.92 |
|
|
Gel content (%) |
GB/T 10437 |
— |
≥60 |
65 |
≥60 |
66 |
|
|
Tensile strength (MPa) |
GB/T 1040 |
ISO 527:1995,IDT |
≥13.5 |
20.0 |
≥13.0 |
23.0 |
|
|
Breaking elongation (%) |
GB/T 1040 |
— |
≥350 |
550 |
≥300 |
580 |
|
|
Brittleness temperature (-76℃, 30 pieces) (Piece) |
GB/T 5470 |
ISO 974:2000 |
≤15/30 |
0/30 |
≤15/30 |
0/30 |
|
|
Hot set elongation (200℃, 0.2MPa, 15min) |
Elongation under load (%) |
GB/T 2951.21 |
IEC 60811-2-1:2001 |
≤100 |
65 |
≤175 |
50 |
|
Permanent deformation after cooling (%) |
≤5 |
0 |
≤15 |
0 |
|||
|
Ageing (135℃, 168h) |
Change of tensile strength (%) |
GB/T 2951.12 |
IEC 60811-1-2:2001 |
≤±20 |
-8 |
≤±20 |
-9.6 |
|
Change of elongation (%) |
≤±20 |
-10 |
≤±20 |
-8.3 |
|||
|
DC volume resistivity (20℃) (Ω.m) |
GB/T 1410 |
IEC 60093:1980 |
≥ 1.0x1014 |
3.0x1014 |
≥5x1013 |
8.0x1014 |
|
|
Dielectric strength (MV/m) |
GB/T 1408.1 |
IEC 602431:1998 |
≥25 |
37 |
≥25 |
34 |
|
|
Dissipation factor (50Hz, 20℃) |
GB/T 1409 |
— |
- |
- |
≤1x10-3 |
3x10-4 |
|